Abstract

In the present work, the microstructural evolution of an APS zirconia stabilized 8% Yttria (8YSZ) coating on Inconel 625 that underwent thermal fatigue from T.A. to 1000°C for 1,500 and 1000 cycles to 1200 °C for 1 and 500 cycles have been. studied. The thickness of the oxide layer that grows during the thermal treatment TGO (Thermally Grown Oxide) increases as the thermal fatigue increases and it seems to be associated with the spallation of the coating. The wavy growth of the TGO was observed due to the thermal cycles. This type of growth generates cracks due to the large compression stresses experimented. The crack formation was clearly observed by atomic force microscopy.


RESUMEN:
En el presente trabajo se estudia la evolución microestructural de un recubrimiento de circona estabilizada con 8% itria (8YSZ) depositado sobre inconel 625 por el método de APS y sometido a ensayos de fatiga térmica desde temperatura ambiente hasta 1000°C por 1, 500 y 1000 ciclos y hasta 1200°C por 1 y 500 ciclos. En las muestras sometidas a los ciclos térmicos se pudo observar que el espesor de la capa de oxido que crece durante tratamiento térmico llamada TGO (Thermally Grown Oxide) va aumentando a medida que aumenta la fatiga térmica y parece estar asociada a la delaminación del recubrimiento. Un crecimiento de forma ondulatoria debido a los ciclos térmicos (500 ciclos) fue observado. Este crecimiento ondulatorio del TGO genera grietas debido a grandes esfuerzos de compresión en el plano experimentados. La formación de grietas sobre el recubrimiento pudo ser observada de manera clara con microscopia de fuerza atómica.